ABS POLYLAC PA-765 Datasheet
ABS POLYLAC PA-765
Technical Data | |||
Product Description | |||
ABS plastic is a kind of "tough, hard and rigid" material with easy-to-obtain raw materials, good comprehensive performance, low price and wide application. ABS plastic has been widely used in machinery, electrical, textile, automobile, aircraft, ship and other manufacturing industries and chemical industry | |||
Physical | Nominal Value Unit | Test Method | |
Density / Specific Gravity | |||
_4 | 1.19g/cm3 | ASTM D792 | |
23°C | 1.19g/cm3 | ISO 1183 | |
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0g/10 min | ASTM D1238 | |
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 58cm3/10min | ISO 1133 | |
Molding Shrinkage | 0.30 to 0.60 % | ISO 294-4 | |
Mechanical | Nominal Value Unit | lest Method | |
Tensile Strength | |||
Yield 5 | 38.1 MPa | ASTM D638 | |
Yield | 38.0 MPa | ISO 527-2/50 | |
Break | 29.0 MPa | ISO 527-2/50 | |
Tensile Elongation | |||
Break 5 | 15% | ASTM D638 | |
Break | 10% | ISO 527-2/50 | |
Flexural Modulus | |||
_6 | 2070 MPa | ASTM D790 | |
_7 | 1800 MPa | ISO 178 | |
Flexural Strength | |||
_6 | 60.7 MPa | ASTM D790 | |
_7 | 55.0 MPa | ISO 178 | |
Impact | Nominal Value Unit | Test Method | |
Charpy Notched Impact Strength | ISO 179 | ||
-30°C | 10kJ/m2 | ||
23°C | 22kJ/m2 | ||
Notched Izod Impact | |||
23°C, 3.20 mm | 210J/m | ASTM D256 | |
23°C, 6.40 mm | 180J/m | ASTM D256 | |
-30°C | 9.0kJ/m2 | ISO 180/1A | |
23°C | 21 kJ/m2 | ISO 180/1A | |
Hardness | Nominal Value Unit | Test Method | |
Rockwell Hardness (R-Scale) | 100 | ASTM D785 | |
Thermal | Nominal Value Unit | Test Method | |
Deflection Temperature Under Load | |||
1.8 MPa, Unannealed | 73.0 °C | ASTM D648 | |
1.8 MPa, Unannealed | 74.0 °C | ISO 75-2/A | |
1.8 MPa, Annealed | 83.0 °C | ASTM D648 ISO 75-2/A | |
Vicat Softening Temperature | |||
— | 90.0°C | ASTM D1525 | |
— | 78.0 °C | ISO 306/B50 | |
— | 91.0°C | ISO 306/A50 | |
CLTE - Flow | 8.4E-5 cm/cm/°C | ISO 11359-2 | |
Flammability | Nominal Value Unit | Test Method | |
Flame Rating | UL 94 | ||
1.0 mm | V-1 | ||
1.5 mm | V-0 | ||
5VB | |||
2.5 mm | 5VA | ||
Injection | Nominal Value Unit | ||
Drying Temperature | 80 to 85 °C | ||
Drying Time | 2.0 to 4.0hr | ||
Rear Temperature | 180 to 210 °C | ||
Middle Temperature | 190 to 220 °C | ||
Front Temperature | 190 to 220 °C | ||
Mold Temperature | 40 to 70 °C | ||
Injection Pressure | 4.90 to 7.85 MPa | ||
Injection Rate | Slow-Moderate | ||
Holding Pressure | 1.96 to 4.90 MPa | ||
Back Pressure | 0.490 to 0.981 MPa | ||
Cushion | 3.18mm | ||